| Composition: | Pd 56.0 / Ag 32.0 / Sn 8.8 / Ga 2.0 / In 1.0 / Ru 0.2 |
| Standard: | DIN EN ISO 22674 and DIN EN ISO 9693 |
| Colour: | white |
| Melting range °C: | 1205–1070 |
| Soft annealing: | 15 mins at 900 °C / quench in water |
| Hardening: | 15 mins at 600 °C / air |
| Preheating temperature °C: | 900 |
| Casting temperature °C: | 1355 |
| Further heating after melting (secs): | electr.: 20–30 inductive: 5–10 flame: 5–10 |
| Density g/cm3: | 11.2 |
| CTE 25°C–500°C (µm/mK): | 14.4 |
| CTE 25°C–600°C (µm/mK): | 14.4 |
| Soldering before firing: | Cehadentor Ceramic solder 1050 |
| Soldering after firing: | Orplid solders 760 |
| Vickers hardness (HV 5/30): | w: 240 a: 280 g/b: 270/250 |
| 0.2% proof stress (MPa): | w: 452 a: 525 g/b: 500/476 |
| Elongation at break (%): | w: 16 a: 11 g/b: 10/13 |
| Spruing: | Following the rules for dental applications (see General Instructions for Use) |
| Investment: | Phosphate-bonded investment materials |
| Preheating: | 900 °C, 30 to 90 mins until end temperature, depending on size of mould |
| Casting: | 1355 °C, possibly increase by 20°C–30°C for resistance-heated vacuum pressure casting. ceramic crucible |
| Finishing: | With carbide burs and/or ceramic-bonded stones. Always grind in one direction only! Sandblasting at a flat angle, using 50–125 µm aluminium oxide. Pressure should not exceed 2 bar |
| Cleaning: | Steam jet cleaning or boiling in distilled water |
| Oxide firing: | 10 mins at 960°C without vacuum |
| Soldering before firing: | Cehadentor Ceramic solder 1050 |
| Soldering after firing: | Orplid solders 760 |
| Firing: | For normally expanding ceramic materials |