Orplid EH

Type 4
yellow / Au 69.0
palladium-free

 

Composition:Au 69.0 / Ag 13.0 / Cu 11.0 / Pt 6.0 / Zn 1.0
Standard:DIN EN ISO 22674
Colour: yellow
Melting range °C:925–890
Soft annealing:15 mins at 750 °C / quench in water
Hardening:15 mins at 450 °C / air
Preheating temperature °C:700
Casting temperature °C:1060
Further heating after melting (secs):electr.: 15–20
inductive: 5–8
flame: 5–8
Density g/cm3:15.5
Solders:Orplid solders 825, 790, 760
Vickers hardness (HV 5/30):w: 175
a: 270
g/b: 270
0.2% proof stress (MPa):w: 385
a: 670
g/b: 660
Elongation at break (%):w: 34
a: 12
g/b: 12
Spruing:Following the rules for dental applications (see General Instructions for Use)
Investment:Phosphate-bonded investment materials (Cehacast P or Cehacast Speed)
Preheating:700 °C, 30 to 120 mins until end temperature, depending on size of mould
Casting:1060 °C, possibly increase by 20°C–30°C for resistance-heated vacuum pressure casting. Graphite crucible or open flame with ceramic crucible.
Finishing:With carbide burs and/or ceramic-bonded stones
Cleaning:Ultrasonic cleaning or steam jet cleaning
Soldering:Orplid solders 825, 790, 760